Contact
Tel: 18037961302
Sales hot line ( 24 hours  service): 18037961302

E-Mail: firstfurnace@gmail.com

whatsapp:+8618037961302

Adress: Luoxin Industrial Park, Luoyang, Henan
  • Products
  • Gear hardening machine

    Large diameter steel pipe quen

    Piston rod quenching and tempe

    Hand-held induction heater

    Grinding rod quenching and tem

    Induction forging machine

    induction heating machine 

    Induction heater

    High frequency induction heate

    Super audio induction heating

    Super audio induction heating

    Guideway quenching integrated

    Quenching equipment for machin

    Round steel end heating furnac

    Steel pipe heat treatment prod

    Square steel quenching and tem

    Sucker rod quenching and tempe

    Thickened petroleum steel pipe

    Round steel quenching and temp

    Steel pipe quenching and tempe

    Steel plate quenching and temp

    Induction Hardening Machine&nb

    Flywheel ring gear high freque

    Oil drill pipe quenching and t

    Iron induction furnace

    Aluminum melting furnace

    Copper melting furnace

    Small steel melting furnace

    Electric furnace technical parameters(²ÎÊý£©
        Composition and characteristics of neutral lining of intermediate frequency furnace
    The refractory material normally used as a neutral lining is a high-alumina refractory material. It is an aluminum silicate refractory material with an Al2O3 content of more than 46%. The equilibrium phase composition of the mass fraction of Al2O3 greater than 71.8% is mullite and corundum, and the liquid phase appears at 1810 ¡ãC. Therefore, it is suitable for use as a lining.
    The mass fraction of the corundum refractory Al2O3 is greater than 95%, and its crystalline form is. ¦Á-Al2O3, which is a hexagonal system, has high chemical stability, is stable in volume at high temperatures, and has a high softening point. Can be used as a lining of more than 10t.
    When melting aluminum and aluminum alloy, the main cause of damage to the lining is the penetration of aluminum; the strong reduction reaction of the elements in the melt on the oxide in the lining. Common lining damage is blackening, nodules and cracking, and this reaction will increase the silicon liquid and affect the composition of the melt. Refractory materials suitable for melting aluminum and aluminum alloys must have good sintering strength, small pore diameter, low content of SiO2, Na2O, K2O, and surface and melt wetting. In addition, the lining should have good sintering properties at a temperature of 800 ¡ãC.
    The aluminum-magnesium dry material is made of fused corundum as the main raw material, and an appropriate amount of MgO and an admixture are added. During the oven and operation, due to the formation of Ai-Mg¡¤S and the structure of the admixture, it can resist the erosion of high temperature molten steel. Compared with MgO, its low thermal expansion rate, coupled with the formation of secondary spinel, can effectively prevent the occurrence of cracks.
    Alumina spinel ramming material is made of high-purity electrolyzed alumina as the main raw material and blended with appropriate amount of high-purity magnesium oxide. It has excellent corrosion resistance and has a specific crystal than magnesium oxide and magnesium aluminum. Stone has a lower coefficient of thermal expansion and good thermal stability. Therefore, it is recommended for medium-frequency induction furnaces for large-scale cast steel of about 6t, and its service life can reach more than 200 heats.

    Copyright© 2007-2013 songdao Electric furnace manufacturing Co,.Ltd All Rights Reserved
    Tel:18037961302 Sales hot line ( 24 hours service): 18037961302
    E-Mail:firstfurnace@gmail.com
    Adress: Luoxin Industrial Park, Luoyang, Henan