Contact
Tel: 18037961302
Sales hot line ( 24 hours  service): 18037961302

E-Mail: firstfurnace@gmail.com

whatsapp:+8618037961302

Adress: Luoxin Industrial Park, Luoyang, Henan
  • Products
  • Gear hardening machine

    Large diameter steel pipe quen

    Piston rod quenching and tempe

    Hand-held induction heater

    Grinding rod quenching and tem

    Induction forging machine

    induction heating machine 

    Induction heater

    High frequency induction heate

    Super audio induction heating

    Super audio induction heating

    Guideway quenching integrated

    Quenching equipment for machin

    Round steel end heating furnac

    Steel pipe heat treatment prod

    Square steel quenching and tem

    Sucker rod quenching and tempe

    Thickened petroleum steel pipe

    Round steel quenching and temp

    Steel pipe quenching and tempe

    Steel plate quenching and temp

    Induction Hardening Machine&nb

    Flywheel ring gear high freque

    Oil drill pipe quenching and t

    Iron induction furnace

    Aluminum melting furnace

    Copper melting furnace

    Small steel melting furnace

    Induction Heating Related Products£¨Ïà¹Ø²úÆ·£©
        

    Quality inspection requirements for gears after quenching by high-frequency quenching equipment

    1. Surface quality

    The teeth should not be over-burned, and then check whether there are cracks in the teeth, 100% inspection for small batches, and inspection for large batches according to the specified ratio.

    2. Surface hardness

    100% inspection for small batches, inspection for large batches according to the specified ratio, generally requiring a hardness of 45-50HRC, and a higher load capacity of 50-56HRC.

    3. Surface organization

    Press ZBJ36 009-88 to check.

    4. Effective hardened layer depth

    Using a Vickers hardness tester, on the cross section of the tooth in the middle of the tooth width: measure from the surface to the inside, the end hardness of the hardened layer is as follows: limit hardness=0.80*minimum surface hardness specified by the design.

    5. Hardened layer distribution

    1) For gears with m<4mm, full tooth hardening is allowed, and the tooth bottom has a certain hardened layer, generally 1.2mm.

    2) For gears with m=4.5-6mm, when using simultaneous heating and quenching, 1/3 tooth height from the tooth root is allowed to be unhardened, and when single tooth is continuously quenched, 1/4 tooth height is allowed to be unhardened.

    3) For gears that are quenched at the same time, the depth of the center hardened layer of the longitudinal section of the gear is more than 2/3 of the depth of the end hardened layer.

    4) When the internal gear m<6mm, the hardened layer is allowed to have a slight slope.

    5) For induction hardened large gears with m>8mm, the hardened tooth height should be 1.7 times the modulus, and when m<8mm, 2/3 tooth height should be hardened.

    This article briefly introduces the inspection items, content and requirements of the quenched gears of the high-frequency quenching equipment. I hope it will be helpful to your work.

    https://songdaokeji.cn/




    Copyright© 2007-2013 songdao Electric furnace manufacturing Co,.Ltd All Rights Reserved
    Tel:18037961302 Sales hot line ( 24 hours service): 18037961302
    E-Mail:firstfurnace@gmail.com
    Adress: Luoxin Industrial Park, Luoyang, Henan