Contact
Tel: 18037961302
Sales hot line ( 24 hours  service): 18037961302

E-Mail: firstfurnace@gmail.com

whatsapp:+8618037961302

Adress: Luoxin Industrial Park, Luoyang, Henan
  • Products
  • Gear hardening machine

    Large diameter steel pipe quen

    Piston rod quenching and tempe

    Hand-held induction heater

    Grinding rod quenching and tem

    Induction forging machine

    induction heating machine 

    Induction heater

    High frequency induction heate

    Super audio induction heating

    Super audio induction heating

    Guideway quenching integrated

    Quenching equipment for machin

    Round steel end heating furnac

    Steel pipe heat treatment prod

    Square steel quenching and tem

    Sucker rod quenching and tempe

    Thickened petroleum steel pipe

    Round steel quenching and temp

    Steel pipe quenching and tempe

    Steel plate quenching and temp

    Induction Hardening Machine&nb

    Flywheel ring gear high freque

    Oil drill pipe quenching and t

    Iron induction furnace

    Aluminum melting furnace

    Copper melting furnace

    Small steel melting furnace

    Induction Heating Related Products£¨Ïà¹Ø²úÆ·£©
        

    Method for surface quenching of forgings

    The surface quenching of the forging is a heat treatment method in which the surface of the workpiece is rapidly heated to the quenching temperature and then rapidly cooled, so that only the surface layer can obtain the quenched structure, while the core part still maintains the structure before quenching. Commonly used are induction heating surface quenching and flame heating surface quenching. Surface hardening is generally medium carbon steel and medium carbon alloy steel forgings.

    Induction hardening uses the principle of electromagnetic induction to induce a huge eddy current on the surface of the workpiece through alternating current, so that the surface of the forging is quickly heated, while the core is hardly heated.

    The characteristics of induction heating surface quenching: after quenching, the martensite grains are refined, and the surface hardness is 2~3HRC higher than ordinary quenching. The surface layer has a large residual compressive stress, which helps to improve the fatigue strength; it is not easy to produce deformation and oxidative decarburization; it is easy to realize mechanization and automation, and is suitable for mass production. After induction heating and quenching, in order to reduce the quenching stress and reduce brittleness, it is necessary to perform low temperature tempering at 170~200¡ãC.

    Flame heating surface quenching is a process in which the surface of forgings is rapidly heated to a phase transition temperature above the phase transition temperature using a flame (temperature as high as 3100~3200¡ãC) burning with oxyacetylene gas, followed by quenching and cooling.

    Low-temperature tempering is carried out immediately after quenching, or the internal waste heat of the forging is used for self-tempering. This method can obtain a hardening depth of 2-6 mm, with simple equipment and low cost, and is suitable for single-piece or small-batch production.

    https://songdaokeji.cn/




    Copyright© 2007-2013 songdao Electric furnace manufacturing Co,.Ltd All Rights Reserved
    Tel:18037961302 Sales hot line ( 24 hours service): 18037961302
    E-Mail:firstfurnace@gmail.com
    Adress: Luoxin Industrial Park, Luoyang, Henan