Contact
Tel: 18037961302
Sales hot line ( 24 hours  service): 18037961302

E-Mail: firstfurnace@gmail.com

whatsapp:+8618037961302

Adress: Luoxin Industrial Park, Luoyang, Henan
  • Products
  • Gear hardening machine

    Large diameter steel pipe quen

    Piston rod quenching and tempe

    Hand-held induction heater

    Grinding rod quenching and tem

    Induction forging machine

    induction heating machine 

    Induction heater

    High frequency induction heate

    Super audio induction heating

    Super audio induction heating

    Guideway quenching integrated

    Quenching equipment for machin

    Round steel end heating furnac

    Steel pipe heat treatment prod

    Square steel quenching and tem

    Sucker rod quenching and tempe

    Thickened petroleum steel pipe

    Round steel quenching and temp

    Steel pipe quenching and tempe

    Steel plate quenching and temp

    Induction Hardening Machine&nb

    Flywheel ring gear high freque

    Oil drill pipe quenching and t

    Iron induction furnace

    Aluminum melting furnace

    Copper melting furnace

    Small steel melting furnace

    Electric furnace technical information£¨¼¼Êõ£©
        

    Traditional spheroidizing annealing process and its existing problems

    The traditional spheroidizing annealing treatment is divided into the following two stages.

    (1) In the preparation stage for spheroidization, the steel to be spheroidized and annealed is heated to 30-50¡ãC above the critical point and held for 1 to 2 hours for austenitization, so that carbides are dissolved into austenite. It is then rapidly cooled to below the critical point Ac to obtain fine crystal grains and refine the carbides to facilitate subsequent spheroidization. Refining grains and refining carbides create conditions for smooth spheroidization, so this stage is called the spheroidization preparation stage. Usually, the preparation stage for spheroidization starts from heating the steel to 850~900¡ãC and holding it for 1~2h, which takes about ten hours in total.

    (2) At the spheroidizing stage, the steel is austenitized and cooled to 700~750¡ãC and kept for about 10 hours, so that the refined carbides will form spherical carbides through cohesion and diffusion, completing the spheroidizing and annealing process.

    From the above spheroidization process, it can be concluded that the eutectoid steel and hypereutectoid steel with higher carbon content, under the action of high temperature for a long time, firstly cause oxidation and decarburization of the steel surface, which reduces the surface quality of the steel; Time spheroidization heat preservation increases energy consumption and reduces production efficiency. Therefore, it is hoped that the rapid spheroidizing annealing process can be studied to shorten the spheroidizing annealing cycle and improve the surface quality of the steel.


    Copyright© 2007-2013 songdao Electric furnace manufacturing Co,.Ltd All Rights Reserved
    Tel:18037961302 Sales hot line ( 24 hours service): 18037961302
    E-Mail:firstfurnace@gmail.com
    Adress: Luoxin Industrial Park, Luoyang, Henan